We demonstrate multi-gigahertz continuous-wave mode-locking of a Yb:KLuW waveguide laser. A femtosecond-laser-inscribed Yb:KLuW channel waveguide in an extended laser cavity delivers a fundamentally mode-locked laser near 1030 nm. A tunable few-centimeter-long cavity containing a single-walled carbon nanotube saturable absorber as mode-locker generates self-starting femtosecond pulses with average output powers exceeding 210 mW at repetition rates of 2.27, 2.69, and 3.55 GHz. The laser cavity, which includes a wedged waveguide, is extended by using a lens pair that controls the laser fluence on the saturable absorber for reliable mode-locked operation without instability. The presented laser performance, mode-locked up to 3.55 GHz, highly suggests the potential of crystalline Yb:KLuW waveguides for realizing high-power ultrafast lasers with higher GHz repetition rates in a quasi-monolithic cavity.

Surface channel waveguides (WGs) were fabricated in a monoclinic Tm3+:KLu(WO4)2 crystal by femtosecond direct laser writing (fs-DLW). The WGs consisted of a half-ring cladding with diameters of 50 and 60 μm located just beneath the crystal surface. They were characterized by confocal laser microscopy and μ-Raman spectroscopy, indicating a reduced crystallinity and stress-induced birefringence of the WG cladding. In continuous-wave (CW) mode, under Ti:sapphire laser pumping at 802 nm, the maximum output power reached 171.1 mW at 1847.4 nm, corresponding to a slope efficiency η of 37.8% for the 60 μm diameter WG. The WG propagation loss was 0.7±0.3 dB/cm. The top surface of the WGs was spin-coated by a polymethyl methacrylate film containing randomly oriented (spaghetti-like) arc-discharge single-walled carbon nanotubes serving as a saturable absorber based on evanescent field coupling. Stable passively Q-switched (PQS) operation was achieved. The PQS 60 μm diameter WG laser generated a record output power of 150 mW at 1846.8 nm with η=34.6%. The conversion efficiency with respect to the CW mode was 87.6%. The best pulse characteristics (energy/duration) were 105.6 nJ/98 ns at a repetition rate of 1.42 MHz.

We report on the operation of passively Q-switched waveguide lasers at 1 μm wavelength based on a graphene/WS2 heterostructure as a saturable absorber (SA). The gain medium is a crystalline Nd:YVO4 cladding waveguide produced by femtosecond laser writing. The nanosecond waveguide laser operation at 1064 nm has been realized with the maximum average output power of 275 mW and slope efficiency of 37%. In comparison with the systems based on single WS2 or graphene SA, the lasing Q-switched by a graphene/WS2 heterostructure SA possesses advantages of a higher pulse energy and enhanced slope efficiency, indicating the promising applications of van der Waals heterostructures for ultrafast photonic devices.